Tantalum Alloy Welding: Does the Thermal Cycle Influence the Microstructure?

Abstract

[EN] The aim of the present work is to verify the microstructural behavior of a B 521 tantalum alloy UNS Grade R05200 after welding, in relation to the welding thermal cycle. The joint design was a 1.5 mm thickness circumferential butt welding, on a 32 mm outside diameter pipe, welded in 1 G position (horizontal, flat, and rotating). The chosen welding process was gas tungsten arc welding (GTAW). The microstructural analysis showed the presence of coarse, dendritic-columnar structures, as well as a hexagonal cell, with no cracks noted. Hardness tests showed an increase in hardness, from 120 HV to 425 HV, in the heat-affected zone. Through finite element methods, the behavior of the temperature field was estimated and compared.